| Material type | Metal |
|---|
| Material name | Aluminum 7075-T651, 3.4365, AlZn5.5MgCu |
|---|
| Process compatibility | CNC machining |
|---|
| Mechanical properties, Ultimate tensile strength | 462 - 538 MPa |
|---|
| Yield strength | 362 - 472 MPa |
|---|
| Elongation at break | 3 - 9 % |
|---|
| Hardness | 150 HB |
|---|
| Thermal properties, Thermal conductivity | 130 W/(m⋅°C) |
|---|
| Post treatments, Anodizing compatibility | Not recommended - due to the high amount of zinc that the material contains, dark spots or corroded marks may be observed |
|---|
Aluminum 7075-T651 | 3.4365 | AlZn5.5MgCu
Aluminum 7075-T651(CNC) is an aerospace-grade material with excellent strength-to-weight ratio and strength and hardness comparable to steels. T651 is the temper of Aluminum 7075, and to achieve this temper, the alloy is solution heat-treated, stress relieved, and then artificially aged.