| Material type | Metal |
|---|
| Material name | Aluminum 7075-T6, AlZn5,5MgCu, 3.4365 |
|---|
| Process compatibility | CNC machining |
|---|
| Ultimate tensile strength | 434 - 580 MPa |
|---|
| Yield strength | 359 - 530 MPa |
|---|
| Young's modulus (modulus of elasticity) | 69 - 76 GPa |
|---|
| Elongation at break | 2 - 11 % |
|---|
| Hardness | 79-86 HRB |
|---|
| Corrosion resistance | Moderate |
|---|
| Magnetism | Non-magnetic |
|---|
| Weldability | Poor |
|---|
| Maximum service temperature | 100 °C |
|---|
| Thermal expansion coefficent | 22,9 - 24,1 10^-6/ºC |
|---|
| Thermal conductivity | 131 - 137 W/(m⋅°C) |
|---|
| Electrical resistivity | 5,2 μΩ*cm |
|---|
| Post-Processing | Annealing & Cold working |
|---|
| Anodizing compatibility | Not recommended - due to the high amount of zinc that the material contains, dark spots or corroded marks may be observed |
|---|
Aluminum 7075-T6 | AlZn5,5MgCu
Aluminum 7075-T6 (CNC) is an aerospace-grade material with excellent strength-to-weight ratio and strength and hardness comparable to steels.
Metal Non-magnetic
| Common applications | Aircraft and aerospace, Marine, Transportation |
|---|